boronisation

基本解釋

This artjcle deals with the effect of alloying elements on the macrostructure,depth,phase compo sition and microhardness of the complex boronisation lamination.
分析并系統(tǒng)研究了合金元素對(duì)復(fù)合硼化層宏觀組織、深度、相成份及顯微硬度的影響。
The effect of technology of heat treatment on the micro-hardness and the phase composition of eom-plex boronisation layer on the O8 steel surface was studied.
分析研究了熱處理工藝對(duì)08鋼復(fù)合硼化層相成分及顯微硬度的影響
Experiment results showed that the process of Hot Dip Aluminum and complex Boronisation on the A3 surface is feasible, it had a continuous layer between diffusion layer and matrix and a better hardness gradient.
試驗(yàn)表明 :A3鋼表面浸鍍擴(kuò)散滲鋁復(fù)合滲硼工藝可行 ,滲層與基體形成了連續(xù)的擴(kuò)散層 ,并且具有良好的硬度梯度。
Keywords Complex boronisation;Macrostructure;Microhardness;
復(fù)合硼化;宏觀組織;微觀硬度;
Keywords die;strengthening and toughening treatment;boronisation;
模具;強(qiáng)韌化處理;滲硼;