die casting

基本解釋

Before I left Buhler within 5 years job is Die Casting Project Manager!
離開布勒前5年的工作是壓鑄機(jī)項(xiàng)目經(jīng)理！
Form and dimension may also be achieved by a number of alternative processes such as hot or cold extrusion, sand casting, die casting, and precision casting.
形式和尺寸也可以通過其它一些可選工藝來達(dá)到，比如熱擠出或冷擠出加工，沙模鑄造，拉模鑄造，或精密鑄造。
Tin welding parts and lead-tin alloy die casting, zinc, beryllium bronze, phosphorus copper alloy in electroplating copper with commonly used before also gets to improve adhesion.
錫焊件、鉛錫合金、鋅壓鑄件、鈹青銅、磷銅等合金在電鍍前也常用預(yù)鍍銅來改善結(jié)合力。

Take Derek Lidderdale, vice president of Omni Die Casting in Massillon, Ohio.
FORBES: The Jobs Gambit
Zinc is also important for die-casting, galvanizing and rubber making and can be used as a paint pigment, wood preservative and agricultural fungicide.
FORBES: Gold Is Good, These Five Metals May Be Better
Casting them adrift to die is much worse.
ECONOMIST: Myanmar’s unwanted human flotsam

壓鑄件
Processing parameters for die casting semi-solid connecting-rod were optimized by simulation. Appropriate processing parameters are as follows:the forming temperature more than 590℃,filling velocity of the ingate more than 2.7m/s and injecting pressure more than 40MPa.
模擬優(yōu)化了連桿壓鑄件的壓鑄工藝,合適的壓鑄工藝參數(shù)為:漿料成形溫度在590℃以上,內(nèi)澆道充填速度為2.7m/s,壓射比壓在40MPa以上。
壓力鑄造
壓鑄模
Design structure of die casting mould was presented, and production ways for part formation were described.
設(shè)計(jì)給出的葉輪壓鑄模結(jié)構(gòu)。
壓鑄工藝
While the part formed by liquid die casting can not be heat treated for its mechanical properties will be sharply reduced after heat treatment.
而液態(tài)壓鑄的零件不能進(jìn)行熱處理，熱處理后材料的力學(xué)性能顯著下降。從對(duì)組織和性能的測(cè)試分析表明：如果半固態(tài)壓鑄工藝得到進(jìn)一步優(yōu)化，零件的力學(xué)性能可以進(jìn)一步提高，半固態(tài)成形后熱處理的作用將會(huì)進(jìn)一步發(fā)揮。
機(jī)械工程
模鑄件
壓模鑄法
壓模鑄造
硬模鑄造
壓力鑄造