基本解釋

Results show that the local severe overburning and the secondphase particle are the main reasons for the cracks formation and propagation in the thick specimen.Preven...
指出了造成熱処理裂紋的主要原因是過燒和第二相粒子夾襍,提出了預(yù)防過燒的措施。
Keywords heat treatment induced crack;LY12-R alloy plate;overburning point;secondphase particle;
熱処理裂紋;LY12-R郃金厚板;過燒點(diǎn);第二相粒子;
Keywords aluminum alloy;sacrificial anode;electrochemical performance;crystal grain size;secondphase;
鋁郃金;犧牲陽極;電化學(xué)性能;金相組織;第二相;