The temperature dependence of the resistivity of the samples was tested from the room temperature(25 ℃) to 300 ℃, and then confirmed using the small-polaron transport model.
測(cè)樣品在常溫（25℃）至300℃范圍內(nèi)的阻溫特性，并利用小極化子導(dǎo)電模型進(jìn)行驗(yàn)證。
Transparent conducting Ti-Ga co-doped zinc oxide films(TGZO) with high transparency and relatively low resistivity have been successfully prepared by DC magnetron sputtering at room temperature.
利用直流磁控濺射工藝在玻璃襯底上成功制備出了透過(guò)率高、電阻率相對(duì)低的鈦鎵共摻雜氧化鋅透明導(dǎo)電薄膜（TGZO）。
The electrical properties of polymeric PTC material filled by PTC ceramics powders were researched, it is found that its′ room-temperature bulk resistivity decreasing and the PTC intensity increasing.
研究了PTC陶瓷粉末摻雜高分子PTC材料的電性能，發(fā)現(xiàn)摻雜后復(fù)合材料的室溫體積電阻率降低、PTC強(qiáng)度增加。